| 厂家(产地)：LG化学 | 牌号：IF870 | 加工级别：注塑级 |
| 特性级别：耐磨 | 用途级别：食品级 | 销售方式：品牌经销 |
| 类型：标准料 |
| 其它 其它 其它 | 外观颜色||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24h | ASTM D-570 | 0.3 | % |
| 物理性能 | 反射指数 | ASTM D-542 | 1.49 | ||
| 比重 | ASTM D-792 | 1.18 | |||
| 透明性 | 3.2mm | ASTM D-1003 | 93 | % | |
| 流动指数 | 230°C,3.8kg | ASTM D-1238 | 23 | g/10min | |
| 机械性能 | 弯曲模数 | ASTM D-790 | 32,000 | Kg/cm2 | |
| 弯曲强度 | ASTM D-790 | 900 | Kg/cm2 | ||
| 拉力 | ASTM D-638 | 650 | Kg/cm2 | ||
| 冲击强度 | Izod Notched | ASTM D-256 | 1.6 | kg· cm/cm2 | |
| 模缩系数 | ASTM D995-51 | 0.2-0.6 | % | ||
| 洛氏硬度 | M-Scale | ASTM D-785 | 84 | ||
| 延伸率 | ASTM D-638 | 2.5 | % | ||
| 电气性能 | 抗体积系数 | ASTM D-257 | >1515 | Ω.m | |
| 功率系数 | 60Hz | ASTM D-150 | 0.05 | ||
| 介电强度 | 4KV/S | ASTM D-149 | KV/mm | KV/mm | |
| 介电定数 | 60Hz | ASTM D-150 | 4 | ||
| 热性能 | 燃烧率 | UL94 | HB | 1/8",1/16" | |
| 维卡软化点 | 18.56kg | ASTM D-648 | 86 | °C | |
| 热传导 | ASTM D-177 | 5×10-4 | cal/seccm· °C/cm | ||
| 绵性膨胀系数 | ASTM D-696 | 6×10 | cm/cm/°C | ||
| 比热 | 0.35 | cal/g/°C | |||
| 热变形温度 | 18.56kg | ASTM D-648 | 86 | °C | |
中文名称:超细PMMA粉
英文名称:Poly(methyl methacrylate)
中文别名:超细聚甲基丙烯酸甲酯粉;聚甲基丙烯酸甲酯;PMMA;聚(甲基甲基丙烯酸酯)
光学级PMMA（聚甲基丙烯酸甲酯）因其优良的透光性、电绝缘性、后加工性等应用广泛，被誉为“塑料女王”。 PMMA高性能光学级液晶材料，主要应用液晶显示器导光板、光纤材料、太阳能光伏电池等高端市场，目前国内只有德国、日本、台湾少数几家外资企业在国内生产，20万吨左右的缺口仍主要靠进口来弥补。
PMMA塑料(有机玻璃) | ||||
英文名称:Polymethyl Methacrylate | (聚甲基丙烯酸甲脂) | |||
比重:1.18克/立方厘米 成型收缩率:0.5-0.7% 成型温度：160-230℃ 干燥条件：70-90℃ 4小时 | ||||
物料性能 | 透明性极好,强度较高,有一定的耐热耐寒性,耐腐蚀,绝缘性良好,综合性能超过聚苯乙烯,但质脆,易熔于有机溶剂,如作透光材料,其表面硬度稍低,容易擦花. | 适于制作透明绝缘零件和强度一般的零件. | ||
成型性能 | 1.无定形料,吸湿大,需干燥,不易分解,流动性中等,易发生填充不良,粘模,收缩,熔接痕等. | |||
2.宜高压注射,在不出现缺陷的条件下取高料温,高模温,以增加流动性,降低内应力,改善透明性及强度.模具浇注系统表面应光洁,脱模斜度大,顶出均匀.同时设排气口,以防出现起泡. | ||||